Bi-Metal Lug 35mm2-Reverse 12mm Stud

Product Description

Reverse Bi-Metal Lug 35MM– (12MM Stud)

The CABAC range of 'Reverse' Bi-Metal Lugs is extensive. In a normal Bi-Metal Lug the palm section is made of Copper but with a reverse Bi-Metal Lug the palm is made of Aluminium and the barrel of Copper.

This range is made from the highest quality Aluminium (99.6%) and Copper (99.9%) then jointed by a friction welding process producing a sound electrical and mechanical joint not subject to electrolysis.

The barrels are chemically treated to reduce contact resistance and corrosion and are filled with a jointing compound breaking the oxide layers on the aluminium. They are designed to be crimped using standard Australian tooling and standard dies.

Standards and Compliance
AS/NZS4325 Part 1; IEC France; DIN/VDE Germany; JIS Japan; BS United Kingdom.

Technical Information


Conductive Material Aluminium Sleeve 99.6% pure Copper Palm 99.9% pure Tensile Strength 110 MPa Ductile Rating 28% Final Metal State Fully Annealed inc. joint Joining Method Friction Welding (IEC std) Dimensional Specification Tooling is interchangeable between CABAC, Utilux and Burndy

Electrical Properties Resistivity 2.6 micro-ohm cm (max): Aluminium 1.738 micro-ohm cm: copper Conductivity 61.8% IACS (min): Aluminium 99.7% IACS: Copper Operating Temperature -40°C to 100°C Torque Recommendations Recommended torques for hardware should be to Australian and New Zealand Standards



Thread dia.(mm)Torque (Nm)

55

69

822

1044

1277

16190


Ordering Information

Line drawings and recommended tooling details are available. See Brochures under Product Resources and select the latest Catalogue.


Part No.Nominal Conductor (mm–)Stud Size

RBL25-102510

RBL25-122512

RBL35-103510

RBL35-123512

RBL50-105010

RBL50-125012

RBL70-107010

RBL70-127012

RBL95-109510

RBL95-129512

RBL120-1012010

RBL120-1212012

RBL150-1015010

RBL150-1215012

RBL185-1018510

RBL185-1218512

RBL240-1024010

RBL240-1224012

RBL300-1030010

RBL300-1230012